UV Stable Solvent Based Polyaspartic
Two component, batch mix aliphatic polyaspartic coating
Long pot life
Moderate tack free time
Good hydrolytic stability up to 160° F
Excellent water resistance
Good resistance to acids and hydrocarbon solvents
Excellent resistance to oxygenated solvents, chlorinated solvents and inorganic bases. See chemical resistant sheet
Produces added luster and clean ability
Intended for use as a clear or colorfast wearing and waterproofing membrane for pedestrian decks, auto decks and industrial flooring.
May be used directly over the ORDuraPatch to provide a less aggressive surface.
Protective coating for feeder bowls.
Protective coating for any metal surfaces.
Apply 5-10 mils over exterior metal surfaces to provide
Chemical resistance-see chemical resistant sheet.
Protection from impact and abrasion on equipment or containers used for hauling various aggregates.
One (1) year in unopened original containers at 40-90° F. Normally, containers should be used within one week after opening unless resealed with nitrogen blanket.
Apply at a rate of 1 gallon per 1200 square feet @ 1 mil. When using granules to provide a higher friction surface, a two coat process can be used. Apply one coat over the CMP I and granules; broadcast additional grit, then topcoat if desired. Prime metal and concrete with OR611 @ 5-10 mil thickness, coverage rate @320-160 S.F. per gallon of primer. Contact CH application specialist for application specifications.
Typical Physical Properties
|Tensile Strength||ASTM D-412||6000|
|Hardness (shore D)||ASTM D-2240||75±3|
|Density B side (dependent on color)||8.7 lbs/gallon|
|Density A side||9.1 lbs/gallon|
|Flash point||above 120° F|
|Viscosity A side||1000 cps @ 23C|
|Viscosity B side||1200 cps @ 23C|
|Coverage||1600 sq ft/gallon/mil.|
|Solids by weight||70-80%|
|Solids by volume||70-80%||(ASTM D-2697)|
|Abrasion Resistant||ASTM-4060-30mg loss|
|Glass water permeability||ASTM D-523||-60°/90+|
|Ultimate Elongation||ASTM D-412||100±25%|
|Tear Resistance (DIE C)||ASTM D-624||225±35pli|
Dry Film Thickness
Exclusive of aggregate @ 1 gal/100 Sq.Ft. 11±2 mils, 279±50 microns
1 part A to 1 part B
Best results are obtained by pouring the part A into the mixing container first, and then mix Polyol into the Part A
Pot life and cure time
Pot life of one gallon quantity is 20-30 min at 70° F. Higher temps and large quantities will shorten pot life and lower temps and smaller quantities will lengthen pot life. When applied at Â½ gallon per sq ft CMP I will be ready for recoat in 1 hour at 70° F. Allow 3-4 hours after final coat before permitting foot traffic.
Can be applied by notched trowel, medium nap roller, squeegee, brush, or spray applied with HLVP or airless
Standard color is clear. Any color is available.
The technical data and any other printed information furnished by Enhanced Flooring Products LLC (EFP LLC) are true and accurate to the best of our knowledge. UV Stable Solvent Based Polyaspartic conforms to in house quality control procedures and should be considered free of defects. The data provided is believed to be reliable and is offered solely for evaluation. The use of this product is beyond the control of the seller therefore the buyer assumes all risks of use and handling whether done in a matter that is in accordance with the provided posted directions or not. EFP LLC makes no warranty; expressed or implied, of its products and shall not be liable for indirect or consequential damage in any event by applicators not certified.
Applicator MUST be certified by EFPLLC for warranty validity